Forintek has completed a two-year investigation of the NLGA SPS 6 Standard, Special Products Standard for Structural Face-Glued Lumber. The NLGA SPS 6 Standard prescribes product specifications and qualification and quality control requirements for structural products created by edge-gluing and/or fingerjoining lumber segments. Under the NLGA SPS 6 Standard, the design values assigned are based on the visual grade and the stress level achieved in qualification tests on the glue joints.
The project assessed the effect of the following three factors on strength of the NLGA SPS 6 product:
1. Tension proof-loading;
2. Relative location of fingerjoints in adjacent members when fingerjoined material is edge-glued;
3. Strength of the material used to make the NLGA SPS 6 product.
Results showed a positive effect of proof-loading, a minor effect of staggering of fingerjoints, and a highly significant effect of density of raw material on tensile stress of edge-glued specimens. It was confirmed that SPS6 products of greater commercial value can be obtained from lower grade lumber. However, visual grading of SPS 6 products proved to be more difficult than visual grading of lumber, because grade-determining wood characteristics were sometimes hidden in the bond line, and could not be properly identified.
The findings of this project can be used to fine tune the NLGA SPS 6 standard and the other NLGA fingerjoint and face-glued lumber product standards. The project will help the wood industry maximize the utilization of their raw material resource, resulting in increased profitability.
Fibre-reinforced wood systems are light, strong, stiff composites that can efficiently replace larger wood members and can be relied on to provide consistent mechanical properties.
This report is an introduction to fibre-reinforced wood systems for members of the Canadian wood products industry. It provides the motivation for reinforcing wood with synthetic fibres, and surveys the choice of materials and their uses. Numerous examples of current applications are discussed to demonstrate the strong and weak points of various approaches and examine the durability and management of fibre-reinforced wood products, as well as to indicate opportunities that exist for the Canadian wood products industry.
This report is intended to be a useful reference for the Canadian wood products industry, and assist future developments in structural and non-structural applications of fibre-reinforced wood products.
The objectives of this project are to provide research information suitable for implementing design procedures for diaphragms with thick sheathing in the Canadian Standard for Engineering Design in Wood (CAN/CSA O86.1) and to make the information available to other markets by publishing the results and recommended procedures in a journal article.
Cross laminated timber (CLT) panels were manufactured and tested to assess their time dependent behaviour. This study is intended to help guide the development of an appropriate test method and acceptance criteria to account for duration of load and creep effects in the design of structures using CLT.
Nine CLT panels of different qualities and using different wood species combinations were manufactured at a pre-commercial pilot plant out of local wood species. The CLT panels manufactured in this study were pressed at about 54% lower pressure than the minimum vertical pressure specified by the adhesive manufacturer due to a limitation of the press, so the CLT panels are viewed as a simulated defective sample, which may occur in a production environment due to material- or process-related issues.
Full-size CLT panels were initially tested non-destructively to assess their bending stiffness. Then, billets were ripped from the full-size CLT panels, and tested to failure in 1-minute and 10-hour ramp tests, or assessed in creep tests under sustained load. The constant loads imposed on the CLT billets tested in creep were calculated as to allow for a maximum deflection of L/180. Following two cycles of loading and relaxation, the CLT billets tested in creep were further tested to failure at the end. The principles of ASTM D6815-09 and those of an in-house FPInnovations protocol were applied to assess the time dependent behavior of the CLT billets.
The main test findings are summarized below:
In terms of residual stiffness, the percentage change in the initial bending stiffness for the CLT billets subjected to the 10-hour ramp test varied between 0-5%, showing a 3% drop in stiffness on average, while that for the CLT billets tested in creep ranged between 0-3%, showing a 1% stiffness drop on average. These are regarded as relatively small changes in bending stiffness.
In general, decreasing creep rates were observed on most of the CLT billets especially in the first cycle up to 90 days. The creep rates went up after 120 days of loading due to an increase in temperature and relative humidity conditions, which greatly affect the rate of deflection and recovery of wood products.
Fractional deflections were calculated for all the CLT billets after 30-day intervals and found to be less than or equal to 1.43.
Creep recovery was above 36% after 30-day, 60-day, and 90-day recovery periods in the first cycle. However, in the second cycle, creep recovery for some CLT billets dropped below 20% for certain time periods.
ASTM D6815-09 provides specifications for evaluation of duration of load and creep effects of wood and wood-based products. The standard was designed to accommodate wood products that can be easily sampled, handled, and tested under load for minimum 90 days and up to 120 days. The standard requires a minimum sample size of 28 specimens. Because of its large dimensions, CLT products are not feasible for experiments requiring such large sample sizes. However, the findings of this study revealed potential for some of the acceptance criteria in ASTM D6815-09 to be applied to CLT products. The CLT billets in this study were assessed in accordance to the creep rate, fractional deflection, and creep recovery criteria in ASTM D6815-09 standard. All CLT billets tested in this study showed (1) decreasing creep rates after 90/120 days of loading, (2) fractional deflections less than 2.0 after 90-day loading, and (3) higher creep recovery than 20% after 30 days of unloading, as required by ASTM D6815-09. A single replicate billet was used per CLT configuration instead of the minimum sample size required by the standard which may have an effect on the findings.